| H13 Grade | |
| Carbon (C) | 0.32 - 0.45% |
| Silicon (Si) | 0.80 - 1.20% |
| Manganese (Mn) | 0.20 - 0.50% |
| Chromium (Cr) | 4.75 - 5.50% |
| Molybdenum (Mo) | 1.10 - 1.75% |
| Vanadium (V) | 0.80 - 1.20% |
| H11 Grade | |
| Carbon (C) | 0.33 - 0.43% |
| Chromium (Cr) | 4.75 - 5.50% |
| Molybdenum (Mo) | 1.10 - 1.60% |
| Vanadium (V) | 0.30 - 0.60% |
| H13 Grade | |
| Hardness (Annealed) | 229 - 255 HB |
| Tensile Strength | 1000 - 1200 MPa |
| Yield Strength | 850 - 1000 MPa |
| Impact Toughness | High |
| H11 Grade | |
| Hardness (Annealed) | 210 - 240 HB |
| Tensile Strength | 900 - 1100 MPa |
| Yield Strength | 750 - 900 MPa |
| D2 Grade | |
| Carbon (C) | 1.40 - 1.60% |
| Silicon (Si) | 0.10 - 0.60% |
| Manganese (Mn) | 0.10 - 0.60% |
| Chromium (Cr) | 11.0 - 13.0% |
| Molybdenum (Mo) | 0.70 - 1.20% |
| Vanadium (V) | 0.50 - 1.10% |
| D3 Grade | |
| Carbon (C) | 2.00 - 2.35% |
| Chromium (Cr) | 11.0 - 13.5% |
| Manganese (Mn) | 0.10 - 0.60% |
| D2 Grade | |
| Hardness (Annealed) | 255 HB |
| Hardness (Hardened) | 58 - 62 HRC |
| Wear Resistance | Excellent |
| D3 Grade | |
| Hardness (Annealed) | 255 HB |
| Hardness (Hardened) | 60 - 64 HRC |
| Abrasion Resistance | Very High |
| M2 Grade | |
| Carbon (C) | 0.78 - 0.88% |
| Tungsten (W) | 5.50 - 6.75% |
| Molybdenum (Mo) | 4.50 - 5.50% |
| Chromium (Cr) | 3.75 - 4.50% |
| Vanadium (V) | 1.75 - 2.20% |
| M35 Grade (with Cobalt) | |
| Carbon (C) | 0.82 - 0.92% |
| Cobalt (Co) | 4.50 - 5.50% |
| M42 Grade (with Cobalt) | |
| Carbon (C) | 1.05 - 1.15% |
| Cobalt (Co) | 7.50 - 8.50% |
| Molybdenum (Mo) | 9.00 - 10.00% |
| M2 Grade | |
| Hardness (Annealed) | 240 - 280 HB |
| Hardness (Hardened) | 63 - 66 HRC |
| M35 Grade | |
| Hardness (Annealed) | 250 - 290 HB |
| Hardness (Hardened) | 64 - 67 HRC |
| M42 Grade | |
| Hardness (Annealed) | 260 - 300 HB |
| Hardness (Hardened) | 65 - 68 HRC |
| MS (Mild Steel) | |
| Carbon (C) | 0.05 - 0.25% |
| Manganese (Mn) | 0.40 - 0.80% |
| EN8 / EN8D | |
| Carbon (C) | 0.36 - 0.44% |
| Manganese (Mn) | 0.60 - 1.00% |
| EN9 | |
| Carbon (C) | 0.50 - 0.60% |
| Manganese (Mn) | 0.50 - 0.80% |
| High Carbon | |
| Carbon (C) | 0.60 - 1.00% |
| MS (Mild Steel) | |
| Tensile Strength | 400 - 550 MPa |
| Yield Strength | 250 MPa |
| EN8 / EN8D | |
| Tensile Strength | 550 - 700 MPa |
| Yield Strength | 280 MPa |
| EN9 | |
| Tensile Strength | 700 - 850 MPa |
| Yield Strength | 370 MPa |
| High Carbon | |
| Tensile Strength | 750 - 1000 MPa |
| Hardness | 200 - 300 HB |
| EN42 | |
| Carbon (C) | 0.65 - 0.75% |
| Manganese (Mn) | 0.60 - 0.90% |
| Silicon (Si) | 0.10 - 0.35% |
| Chromium (Cr) | 0.20 - 0.40% |
| EN47 | |
| Carbon (C) | 0.45 - 0.55% |
| Silicon (Si) | 1.50 - 2.00% |
| Chromium (Cr) | 0.80 - 1.20% |
| Manganese (Mn) | 0.50 - 0.80% |
| EN42 | |
| Tensile Strength | 1000 - 1200 MPa |
| Elongation | 10% |
| Elasticity | High |
| EN47 | |
| Tensile Strength | 900 - 1100 MPa |
| Hardness | 250 - 300 HB |
| Fatigue Resistance | Excellent |
| EN353 | |
| Carbon (C) | 0.14 - 0.20% |
| Manganese (Mn) | 0.60 - 1.00% |
| Chromium (Cr) | 0.75 - 1.25% |
| Nickel (Ni) | 1.00 - 1.50% |
| Molybdenum (Mo) | 0.08 - 0.15% |
| 8620 | |
| Carbon (C) | 0.18 - 0.23% |
| Chromium (Cr) | 0.40 - 0.60% |
| Nickel (Ni) | 0.40 - 0.70% |
| Molybdenum (Mo) | 0.15 - 0.25% |
| 20MNCR5 | |
| Carbon (C) | 0.17 - 0.22% |
| Manganese (Mn) | 1.10 - 1.40% |
| Chromium (Cr) | 1.00 - 1.30% |
| 16MNCR5 | |
| Carbon (C) | 0.14 - 0.19% |
| Manganese (Mn) | 1.00 - 1.30% |
| Chromium (Cr) | 0.80 - 1.10% |
| EN353 | |
| Core Tensile Strength | 700 - 900 MPa |
| Surface Hardness | 60 - 62 HRC |
| 8620 | |
| Core Tensile Strength | 650 - 850 MPa |
| Surface Hardness | 58 - 62 HRC |
| 20MNCR5 / 16MNCR5 | |
| Core Tensile Strength | 650 - 900 MPa |
| Surface Hardness | 58 - 62 HRC |
| Core Toughness | High |
| EN24 | |
| Carbon (C) | 0.35 - 0.45% |
| Chromium (Cr) | 0.90 - 1.40% |
| Nickel (Ni) | 1.30 - 1.80% |
| Molybdenum (Mo) | 0.20 - 0.35% |
| EN19 | |
| Carbon (C) | 0.35 - 0.45% |
| Chromium (Cr) | 0.90 - 1.50% |
| Molybdenum (Mo) | 0.20 - 0.35% |
| EN31 | |
| Carbon (C) | 0.90 - 1.20% |
| Chromium (Cr) | 1.00 - 1.60% |
| Manganese (Mn) | 0.30 - 0.75% |
| EN24 | |
| Tensile Strength | 850 - 1000 MPa |
| Yield Strength | 680 MPa |
| EN19 | |
| Tensile Strength | 700 - 850 MPa |
| Yield Strength | 500 MPa |
| EN31 | |
| Hardness (Annealed) | 229 - 269 HB |
| Hardness (Hardened) | 58 - 62 HRC |